Roller Hatua Shaft
Maelezo ya Bidhaa:
Mahali pa asili: Shanxi
Jina la Biashara: DHZ
Uthibitishaji: ASME, JIS, DIN, GB, BS, EN, AS, SABS, ASTM A370, API 6B, API 6C
Ripoti ya Majaribio: MTC, HT, UT, MPT, Dimension Report, Visual Test, EN10204-3.1, EN10204-3.2
Kiwango cha chini cha Agizo: kipande 1
Ukali wa Uso wa Jarida: 0.63-0.16μm
Muonekano wa sura: Mviringo
Kifurushi cha Usafiri: Kesi ya Plywood
Bei: Inaweza kujadiliwa
Uwezo wa Uzalishaji: 100PCS / Mwezi
| Vipengele vya nyenzo | C | Mn | P | S | SI | Cr | NI | Mo | Cu | N |
| 4130 | 0.33 | 0.7 | <0.025 | <0.025 | <0.35 | 0.8-1.0 | <0.5 | 0.15-0.25 | / | / |
| A182 F53 | ≤ 0.030 | ≤ 1.20 | ≤ 0.035 | <0.020 | <0.80 | 24-26 | 6.0-8.0 | 3-5 | <0.50 | 0.24-0.32 |
| A105 | 0.19-0.23 | 0.9-1.05 | ≤ 0.035 | ≤ 0.030 | 0.15-0.3 | ≤ 0.1 | ≤ 0.4 | ≤ 0.12 | ≤ 0.4 | / |
| F6Mn | ≤ 0.05 | 1.0 | ≤ 0.03 | ≤0.03 | ≤0.60 | 11-14 | 3.5-5.5 | 0.5-1 | / | / |
| 42CrMo4 | 0.43 | 1.0 | <0.030 | <0.040 | <0.35 | 0.8-1.1 | <0.030 | 0.15-0.25 | / | / |
| 34CrNiMo6 | 0.3-0.38 | 0.5-0.8 | ≤ 0.025 | ≤ 0.035 | ≤ 0.4 | 1.3-1.7 | 1.3-1.7 | 0.15-0.3 | / | / |
| 09G2S ( 09Г2С ) | ≤ 0.12 | 1.3-1.7 | ≤ 0.03 | ≤ 0.035 | 0.5-0.8 | ≤ 0.3 | ≤ 0.3 | / | ≤ 0.3 | ≤ 0.008 |
| ASMA36 | ≤ 0.26 | 0.6-0.9 | ≤ 0.040 | ≤ 0.050 | ≤ 0.40 | / | / | / | ≥0.20 | / |
| Mali ya mitambo | Dia.(mm) | TS/Rm (Mpa) | YS/Rp0.2 (Mpa) | EL/A5 (%) | RA/Z (%) | Notch | Nishati ya athari | HBW |
| 4130 | Ф10 | = 655 | 517 | ＞18 | ＞35 | V | ≥20J(-60℃) | 197-23 |
| A182 F53 | / | ≥800 | ≥550 | ≥15 | / | V | / | <310 |
| A105 | / | ≥485 | ≥250 | ≥22 | ≥30 | V | / | 143-187 |
| F6Mn | / | ≥790 | ≥620 | ≥15 | ≥45 | V | / | ≤295 |
| 42CrMo4 | Ф10 | ~1080 | 930 | ＞25 | ＞45 | V | ≥25J(-60℃) | <217 |
| 34CrNiMo6 | Ф12.5 | ≥785 | / | ≥11 | ≥30 | V | ≥71J | / |
| 09G2S ( 09Г2С ) | Ф25 | 900-1050 | ≥700 | ≥10 | ≥50 | V | / | / |
| ASMA36 | / | 400-550 | ≥250 | ≥23 | / | V | / | / |
Taratibu za Uzalishaji:
Mchakato wa kuunda udhibiti wa ubora wa mtiririko: Chuma cha malighafi huingia kwenye ghala(jaribu maudhui ya kemikali) → Kukata→ Kupasha joto(Jaribio la joto la tanuru) → Matibabu ya joto baada ya kughushi(Jaribio la joto la tanuru) Toa tanuru(ukaguzi tupu)→Machining→ Ukaguzi(UT ,MT,kipenyo cha macho, ugumu)→ QT→ Ukaguzi(UT, sifa za mitambo, ugumu, saizi ya nafaka)→ Maliza kutengeneza→Kagua (kipimo)→ Ufungashaji na Uwekaji Alama(muhuri wa chuma, alama)→ Usafirishaji wa Hifadhi
Faida:
Tabia bora za mitambo,
Uvumilivu wa hali ya juu wa usahihi,
Kudhibiti utaratibu wa uzalishaji madhubuti,
Vifaa vya juu vya utengenezaji na vifaa vya ukaguzi,
Mtu bora wa kiufundi,
Tengeneza vipimo tofauti kulingana na mahitaji ya mteja,
Makini na ulinzi wa kifurushi,
Ubora wa huduma kamili.
Sekta ya Maombi:
Uchimbaji wa mafuta na gesi, uzalishaji wa nishati ya upepo, mitambo ya metallurgiska, mitambo ya uhandisi, sekta ya ujenzi wa meli, vyombo vya shinikizo, nguvu za nyuklia, n.k.