Pete Kubwa Nusu-pete
Maelezo ya Bidhaa:
Mahali pa asili: Shanxi
Jina la Biashara: DHZ
Uthibitishaji: ASME, JIS, DIN, GB, BS, EN, AS, SABS, ASTM A370, API 6B, API 6C
Kiwango cha chini cha Agizo: kipande 1
Ukubwa mbalimbali: Max OD4000mm
Kifurushi cha Usafiri: Kesi ya Plywood
Ripoti ya Majaribio: MTC, HT, UT, MPT, Dimension Report, Visual Test, EN10204-3.1, EN10204-3.2
Bei:Inaweza kujadiliwa
Uwezo wa Uzalishaji: PCS 100 / Mwezi
| Vipengele vya nyenzo | C | Mn | P | S | SI | Cr | NI | Mo | Cu | N |
| A182 F51 | ≤ 0.030 | 2.0 | ≤ 0.030 | ≤ 0.020 | <0.80 | 21-23 | 4.5-6.5 | 2.50-3.50 | / | 0.20-0.24 |
| A105 | 0.19-0.23 | 0.9-1.05 | ≤ 0.035 | ≤ 0.030 | 0.15-0.3 | ≤ 0.1 | ≤ 0.4 | ≤ 0.12 | ≤ 0.4 | / |
| LF2 | 0.19-0.23 | 0.9-1.05 | ≤ 0.035 | ≤ 0.030 | 0.15-0.3 | ≤ 0.1 | ≤ 0.4 | ≤ 0.12 | ≤ 0.4 | / |
| 42CrMo4 | 0.43 | 1.0 | <0.030 | <0.040 | <0.35 | 0.8-1.1 | <0.030 | 0.15-0.25 | / | / |
| 35NiCrMoV12-5 | 0.30-0.40 | 0.4-0.7 | ≤ 0.015 | ≤ 0.015 | ≤ 0.35 | 1.0-1.4 | 2.5-3.5 | 0.35-0.65 | / | / |
| 20MnMo | 0.17-0.23 | 1.1-1.4 | ≤0.025 | ≤0.015 | 0.17-0.37 | ≤0.030 | ≤0.030 | 0.20-0.35 | / | / |
| Mali ya mitambo | Dia.(mm) | TS/Rm (Mpa) | YS/Rp0.2 (Mpa) | EL/A5 (%) | RA/Z (%) | Notch | Nishati ya athari | HBW |
| A182 F51 | / | ≥620 | ≥450 | ≥25 | ＞45 | V | ≥45J | / |
| A105 | / | ≥485 | ≥250 | ≥22 | ≥30 | V | / | 143-187 |
| LF2 | / | 485-655 | ≥250 | ≥22 | ≥30 | V | ≥27J(-29℃) | 143-187 |
| 42CrMo4 | Ф10 | ~1080 | 930 | ＞25 | ＞45 | V | ≥25J(-60℃) | <217 |
| 35NiCrMoV12-5 | Ф12.5 | ≥1100 | ≥850 | ≥8.0 | / | V | / | / |
| 20MnMo | Ф10 | ≥605 | ≥475 | ≥25 | / | V | ≥180 | / |
Taratibu za Uzalishaji:
Mchakato wa kuunda udhibiti wa ubora wa mtiririko: Chuma cha malighafi huingia kwenye ghala(jaribu maudhui ya kemikali) → Kukata→ Kupasha joto(Jaribio la joto la tanuru) → Matibabu ya joto baada ya kughushi(Jaribio la joto la tanuru) Toa tanuru(ukaguzi tupu)→Machining→ Ukaguzi(UT ,MT,kipenyo cha macho, ugumu)→ QT→ Ukaguzi(UT, sifa za mitambo, ugumu, saizi ya nafaka)→ Maliza kutengeneza→Kagua (kipimo)→ Ufungashaji na Uwekaji Alama(muhuri wa chuma, alama)→ Usafirishaji wa Hifadhi
Faida:
Tabia bora za mitambo,
Uvumilivu wa hali ya juu wa usahihi,
Kudhibiti utaratibu wa uzalishaji madhubuti,
Vifaa vya juu vya utengenezaji na vifaa vya ukaguzi,
Mtu bora wa kiufundi,
Tengeneza vipimo tofauti kulingana na mahitaji ya mteja,
Makini na ulinzi wa kifurushi,
Ubora wa huduma kamili.
Sekta ya Maombi:
Sekta ya Petrokemikali, tasnia ya kijeshi, moduli za viwanda, sekta ya injini, majukwaa ya nje ya nchi, usindikaji wa sehemu, tasnia ya magari, vifaa vya matibabu, n.k.