Modrwy Gêr Dur aloi
Manylion Cynnyrch:
Man Tarddiad: Shanxi
Enw Brand: DHDZ
Ardystiad: ASME, JIS, DIN, GB, BS, EN, UG, SABS, ASTM A370, API 6B, API 6C
Adroddiad Profi: MTC, HT, UT, MPT, Adroddiad Dimensiwn, Prawf Gweledol, EN10204-3.1, EN10204-3.2
Isafswm Gorchymyn Nifer: 1 darn
Pecyn Trafnidiaeth: Achos Pren haenog
Pris: Trafodadwy
Cynhwysedd Cynhyrchu: 100PCS / Mis
| Elfennau materol | C | Mn | P | S | SI | Cr | NI | Mo | Cu | N |
| 4140 | 0.43 | 1.0 | <0.030 | <0.040 | <0.35 | 0.8-1.1 | <0.030 | 0.15-0.25 | <0.030 | / |
| F6Mn | ≤ 0.05 | 1.0 | ≤ 0.03 | ≤0.03 | ≤0.60 | 11-14 | 3.5-5.5 | 0.5-1 | / | / |
| 09G2S ( 09Г2С ) | ≤ 0.12 | 1.3-1.7 | ≤ 0.03 | ≤ 0.035 | 0.5-0.8 | ≤ 0.3 | ≤ 0.3 | / | ≤ 0.3 | ≤ 0.008 |
| 35NiCrMoV12-5 | 0.30-0.40 | 0.4-0.7 | ≤ 0.015 | ≤ 0.015 | ≤ 0.35 | 1.0-1.4 | 2.5-3.5 | 0.35-0.65 | / | / |
| 20MnMo | 0.17-0.23 | 1.1-1.4 | ≤0.025 | ≤0.015 | 0.17-0.37 | ≤0.030 | ≤0.030 | 0.20-0.35 | / | / |
| 20MnMoNo | 0.16-0.23 | 1.2-1.5 | ≤0.035 | ≤0.035 | 0.17-0.37 | / | / | 0.45-0.60 | / | 0.20-0.45 |
| Eiddo mecanyddol | Dia.(mm) | TS/Rm (Mpa) | YS/Rp0.2 (Mpa) | EL/A5 (%) | RA/Z (%) | Rhic | Effaith ynni | HBW |
| 4140 | Ф10 | ＞ 1080 | ＞ 930 | ＞ 25 | ＞ 45 | V | ≥25J (-60 ℃) | <217 |
| F6Mn | / | ≥790 | ≥620 | ≥15 | ≥45 | V | / | ≤295 |
| 09G2S ( 09Г2С ) | Ф25 | 900-1050 | ≥700 | ≥10 | ≥50 | V | / | / |
| 35NiCrMoV12-5 | Ф12.5 | ≥1100 | ≥850 | ≥8.0 | / | V | / | / |
| 20MnMo | Ф10 | ≥605 | ≥475 | ≥25 | / | V | ≥180 | / |
| 20MnMoNo | Ф10 | ≥635 | ≥490 | ≥15 | / | U | ≥47 | 187-229 |
Gweithdrefnau Cynhyrchu:
Rheoli ansawdd llif y broses ffugio: Ingot dur deunydd crai i'r warws (profwch y cynnwys cemegol) → Torri → Gwresogi (prawf tymheredd y ffwrnais) → Triniaeth wres ar ôl gofannu (Prawf tymheredd y ffwrnais) Gollwng y ffwrnais (archwiliad gwag) → Peiriannu → Archwiliad (UT , MT, Diamention gweledol, caledwch) → QT→ Archwiliad (UT, priodweddau mecanyddol, caledwch, maint grawn) → Peiriannu gorffen → Arolygu (dimensiwn) → Pacio a Marcio (stamp dur, marc) → Cludo Storio
Mantais:
Priodweddau mecanyddol rhagorol,
Goddefgarwch dimensiwn manwl uchel,
Rheoli'r weithdrefn gynhyrchu yn llym,
Offer gweithgynhyrchu uwch a dyfeisiau archwilio,
Personoliaeth dechnegol ardderchog,
Cynhyrchu dimensiwn gwahanol yn seiliedig ar ofynion y cwsmer,
Rhowch sylw i amddiffyniad y pecyn,
Gwasanaeth llawn o safon.