9 cr2mo materials for typical Cr2 cold roll steel is mainly in the industrial used in the manufacture of cold rolled with the roller of roller of cold die and punch etc forging but many say don't know about 9 cr2mo heat treatment method, so here mainly to talk about 9 cr2mo heat treatment method, hope to be of spheroidizing annealing: 1 790 ~ 810 heating, isothermal, 650 ~ 670, 500 from air cooling;2 Quenching: Suhu pemanasan = 880 ~ 900, pendinginan pendinginan: Menurut berbagai pengampunan dan persyaratan yang berbeda, media pendingin seperti oli cairan pendinginan air PAG dapat digunakan.
CATATAN: The Forgings adalah CR2 Cold Roll Steel khas。

https://www.shdhforging.com/flanges/

3 Suhu Titik Kritis (Nilai Perkiraan): AC1 = 740 C AR1 = 700 C ACCM: 850 C 4 Spesifikasi pelunakan umum untuk Cold Pressed Blank:(820 10) C 3 ~ 4H, dengan laju pendinginan.15 C /H, dengan tungku perlahan-lahan mendingin hingga 650 C, 5 Cold Pressed Blank dari pendingin oven ke spesifikasi pelunakan spindle spindle:(820 10) C 3 ~ 4H, (720 10) C 6 ~ 8H, kemudian dengan tungku perlahan-lahan mendingin hingga 600 C, spesifikasi untuk menormalkan: normalisasi suhu 900 ~ 920 C, Kekerasan 302-388HBW 7 Batch Isothermal Annealing: 790 ~ 810 C 2 ~ 3H, pendinginan tungku, 7ohliss 3 ~ 790-49 ~ 810 C 2 ~ 3H, pendingin tungku, 7oHl, 7O0- 490-47 ~ 810 C 2 ~ 3H, tungku, 7oh. 790-47 ~ 810 C 2 ~ 3H, FURNACE, 7O0- 490-47 ~ 810 C 2 ~ 3H, FURCHACE, 7O0- 49 ~ 810 C 2 ~ 3H, 7oH. tissue grade 2-5,Specification for quenching and tempering of 8 forgings of mesh carbide grade 2 1. Quenching temperature 830-850 C, hardness 62-65 HRC, tempering temperature 130-150 C, hardness 62-65 HRC 2. Quenching temperature 840-860 C, hardness 61-63 HRC, tempering temperature 150-170 C, hardness 60-62HRC.


Waktu posting: AGUG-04-2020

  • Sebelumnya:
  • Berikutnya: