China wholesale Heavy Alloy Steel Forgings - Forged Discs – DHDZ
China wholesale Heavy Alloy Steel Forgings - Forged Discs – DHDZ Detail:
Open Die Forgings Manufacturer In China
Forged Disc
Gear blanks, flanges, end caps, pressure vessel components, valve components, valve bodies, and piping applications. Forged disks are superior in quality to disks cut from plate or bar due to all sides of the disk having forging reduction further refining the grain structure and improving the materials impact strength and fatigue life. Furthermore forged disks can be forged with grain flow to best suit the final parts applications such as radial or tangential grain flow which will help improve the mechanical properties of the material.
Common used material: 1045 | 4130 | 4140 | 4340 | 5120 | 8620 | 42CrMo4 | 1.7225 | 34CrAlNi7 | S355J2 | 30NiCrMo12 |22NiCrMoV
FORGED DISC
Large press forged blocks up to 1500mm x 1500mm section with variable length.
Block forging tolerance typically -0/+3mm up to +10mm dependent on size.
●All Metals has the forging capabilities to produce bars from the following alloy types:
● Alloy steel
● Carbon steel
●Stainless steel
FORGED DISCS CAPABILITIES
Material
MAX DIAMETER
MAX WEIGHT
Carbon, Alloy Steel
3500mm
20000 kgs
Stainless Steel
3500mm
18000 kgs
Shanxi DongHuang Wind Power Flange Manufacturing Co., LTD. , as an ISO registered certified forging manufacturer, guarantee that the forgings and/or bars are homogenous in quality and free of anomalies which are detrimental to the mechanical properties or machining properies of the material.
Case:
Steel Grade SA 266 Gr 2
Chemical composition % of steel SA 266 Gr 2 |
||||
C |
Si |
Mn |
P |
S |
Max 0.3 |
0.15 – 0.35 |
0.8- 1.35 |
max 0.025 |
max 0.015 |
Applications
Gear blanks, flanges, end caps, pressure vessel components, valve components, valve bodies, and piping applications
Delivery form
Forged disc, Forged Disk
SA 266 Gr 4 Forged disc, Carbon steel forgings for pressure vessels
Size: φ1300 x thk 180mm
Forging (Hot Work ) Practice, Heat Treatment Procedure
Forging |
1093-1205℃ |
Annealing |
778-843℃ furnace cool |
Tempering |
399-649℃ |
Normalizing |
871-898℃ air cool |
Austenize |
815-843℃ water quench |
Stress Relieve |
552-663℃ |
Quenching |
552-663℃ |
Rm - Tensile strength (MPa) (N) |
530 |
Rp0.2 0.2% proof strength (MPa) (N) |
320 |
A - Min. elongation at fracture (%) (N) |
31 |
Z - Reduction in cross section on fracture (%) (N) |
52 |
Brinell hardness (HBW): | 167 |
ADDITIONAL INFORMATION
REQUEST A QUOTE TODAY
OR CALL: 86-21-52859349
Product detail pictures:
Related Product Guide:
Our target should be to consolidate and enhance the top quality and service of current goods, in the meantime frequently create new products to satisfy diverse customers' calls for for China wholesale Heavy Alloy Steel Forgings - Forged Discs – DHDZ , The product will supply to all over the world, such as: Nigeria, Belgium, Bolivia, We strongly believe that technology and service is our base today and quality will create our reliable walls of future. Only we've got better and better quality , could we achieve our customers and ourselves, too. Welcome customers all over the word to contact us for getting further business and reliable relationships. We have been always here working for your demands whenever you require.
By Honey from Hongkong - 2017.09.29 11:19
This company has the idea of "better quality, lower processing costs, prices are more reasonable", so they have competitive product quality and price, that's the main reason we chose to cooperate.
By Jessie from Haiti - 2018.07.27 12:26